Asphalt Shingle

Asphalt shingles are an American invention first used in 1901, in general use in parts of America by 1911 and by 1939 11 million squares of shingles were being produced.  A U.S. National Board of Fire Underwriters campaign to eliminate the use of wood shingles on roofs was a contributing factor in the growth in popularity of asphalt shingles during the 1920s. The forerunner of these shingles was first developed in 1893 and called asphalt prepared roofing which was similar to asphalt roll roofing without the surface granules. In 1897 slate granules were added to the surface to make the material more durable. Types of granules tested have included mica, oyster shells, slate, dolomite, fly-ash, silica and clay. In 1901 this material was first cut into strips for use as one-tab and multi-tab shingles.

All shingles were organic at first with the base material, called felt, being primarily cotton rag until the 1920s when cotton rag became more expensive and alternative materials were used. Other organic materials used as the felt included wool, jute or manila, and wood pulp. In 1926 the Asphalt Shingle and Research Institute with the National Bureau of Standards tested twenty two types of experimental felts and found no significant differences in performance. In the 1950s self-sealing and manually applied adhesives began to be used to help prevent wind damage to shingle roofs. The design standard was for the self-sealing strips of adhesive to be fully adhered after sixteen hours at 140 degrees Fahrenheit. Also in the 1950s testing on the use of 3/4 inch staples rather than roofing nails was carried out showing they could perform as well as nails but with six staples compared with four nails.In 1960 fiberglass mat bases were introduced with limited success; the lighter, more flexible fiberglass shingles proved to be more susceptible to wind damage particularly at freezing temperatures. Later generations of shingles constructed using fiberglass in place of asbestos provided acceptable durability and fireproofing. Also in the 1960s research into hail damage which was found to occur when hail reach a size larger than 1.5 inches.

Asphalt Roofing Manufacturers Association (ARMA) formed the High Wind Task Force in 1990 to continue research to improve shingle wind resistance. In 1996, a partnership between members of the U.S. property insurance industry, the Institute of Business and Home Safety, and the Underwriter’s Laboratory (UL) was established to create an impact resistance classification system for roofing materials. The system, known as UL 2218, established a national standard for impact resistance. Subsequently, insurers offered discounted premiums for policies on structures using shingles that carried the highest impact classification (class 4). In 1998, Texas Insurance Commissioner Elton Bomer mandated that Texas provide premium discounts to policyholders that installed class 4 roofs.

Two types of base materials are used to make asphalt shingles, organic and fiberglass. Both are made in a similar manner, with an asphalt-saturated base covered on one or both sides with asphalt or modified-asphalt, the exposed surface impregnated with slate, schist, quartz, vitrified brick, stone, or ceramic granules, and the under-side treated with sand, talc or mica to prevent shingles from sticking to one-another before use.

The top surface granules block ultra-violet light, which causes the shingles to deteriorate, provides some physical protection of the asphalt core, and provides color – lighter shades preferred for their heat reflectivity in sunny climates, darker in cooler ones for their asborption. Some shingles have copper or other biocides added to the surface to help prevent algae growth. Self-sealing strips are standard on the underside of shingles to provide resistance to lifting in high winds. This material is typically limestone or fly-ash-modified resins, or polymer-modified bitumen. American Society of Civil Engineers ASTM D7158 is the standard most United States residential building codes use as their wind resistance standard for most discontinuous, steep-slope roof coverings (including asphalt shingles) with the following class ratings: Class D – Passed at basic wind speeds up to and including 90 mph; Class G – Passed at basic wind speeds up to and including 120 mph; and Class H – Passed at basic wind speeds up to and including 150 mph. An additive known as styrene-butadiene-styrene (SBS), sometimes called modified or rubberized asphalt, is sometimes added to the asphalt mixture to make shingles more pliable, resistant to thermal cracking, and more resistant to damage from hail impacts. Some manufacturers use a fabric backing known as a scrim on the back side of shingles to make them more impact resistant. Most insurance companies offer discounts to homeowners for using Class 4 impact rated shingles.

Organic

Organic shingles are made with a base mat of organic materials such as waste paper, cellulose, wood fiber, or other materials. This is saturated with asphalt to make it waterproof, then a top coating of adhesive asphalt is applied, covered withd solid granules. Such shingles contain around 40% more asphalt per square (100 sq ft.) than fiberglass shingles. Their organic core leaves them more prone to fire damage, resulting in a maximum class “B” FM fire rating. They are also less brittle than fiberglass shingles in cold weather.

The early wood material-based versions were very durable and hard to tear, an important quality before self-sealing materials were added to the underside of shingles to bond them to the layer beneath. Also, some organic shingles produced before the early 1980s may contain asbestos.

Fiberglass

Fiberglass reinforcement was devised as the replacement for asbestos in organic mat shingles. Fiberglass shingles have a base layer of glass fiber reinforcing mat made from wet, random-laid glass fibers bonded with ureaformaldehyde resin. The mat is then coated with asphalt containing mineral fillers to make it waterproof. Such shingles resist fire better than those with organic/paper mats, making them eligible for as high as a class “A” rating. Weight typically ranges from 1.8 to 2.3 pounds/square foot.

Fiberglass shingles gradually began to replace organic felt shingles, and by 1982 overtook them in use. Widespread hurricane damage in Florida during the 1990s prompted the industry to adhere to a 1700-gram tear value on finished asphalt shingles.

Per 2003 International Building Code Sections 1507.2.1 and 1507.2.2, asphalt shingles shall only be used on roof slopes of two units vertical in 12 units horizontal (17% slope) or greater. Asphalt shingles shall be fastened to solidly sheathed decks. Shallower slopes require asphalt rolled roofing, or other roofing treatment.

Architectural or 3-Tab

Asphalt Shingles come in two standard design options: Architectural (also known as Dimensional) Shingles, and 3-Tab Shingles. 3-Tab are essentially flat simple shingles with a uniform shape and size. They use less material and are thinner than Architectural Shingles, and are therefore lighter and lower cost for both the material and the installation. They also do not last as long or offer Manufacturer’s Warranties as long as good architectural asphalt shingles. 3-Tab are still the most commonly installed in lower-value homes, such as those used as rental properties. However, they are declining in popularity in favor of the architectural style. Dimensional, or architectural shingles are thicker and stronger, vary in shape and size, and offer more aesthetic appeal; casting more distinct, random shadow lines better mimics the appearance of traditional roofing materials such as wood shake shingles. The result is a more natural, traditional look. While more expensive to install, they come with longer manufacturer’s warranties, sometimes up to 50 Years – typically prorated, as virtually all asphalt shingle roofs are replaced before such an expiration could be reached. While 3-tab shingles typically need to be replaced after 15–18 years, Dimensional typically last 24–30 years.